Low Smoke Zero Halogen Irradiated Insulating Cable Material - High-Quality China Suppliers and Factory
PRODUCT FEATURES
SCOPE OF USE
Cable and optical cable, coaxial cable, network cable, elevator cable, etc.
TEST ITEMS AND STANDARDS
Properties of halogen-free low smoke flame retardant thermoplastic polyolefin insulating materials and sheathing materials.
| No. | Inspection item | Unit | Requirements | ||
|---|---|---|---|---|---|
| WDZ-Y-J70 | WDZ-Y-H70 | WDZ-Y-H90 | |||
| 1 | Tensile strength | MPa | ≥10.0 | ≥10.0 | ≥10.0 |
| 2 | Elongation at break | % | ≥160 | ≥160 | ≥160 |
| 3 | Air aging chamber | ||||
| Aging temperature | ℃ | 100±2 | 100±2 | 110±2 | |
| Aging time | h | 168 | 168 | 240 | |
| Maximum rate of change of tensile strength | % | ±25 | ±25 | ±25 | |
| Maximum rate of change of elongation at break | % | ±25 | ±25 | ±25 | |
| 4 | Thermal deformation | ||||
| Test temperature | ℃ | 90±2 | 90±2 | 90±2 | |
| Experimental result | % | ≤50 | ≤50 | ≤50 | |
| 5 | 20℃ volume resistivity | Ω·m | ≥1.0×1012 | ≥1.0×1010 | ≥1.0×1010 |
| 6 | Volume resistivity at operating temperature | ||||
| Test temperature | ℃ | 70±1 | — | — | |
| Volume resistivity | Ω·m | ≥2.0×108 | — | — | |
| 7 | Dielectric strength | MV/m | ≥20 | ≥18 | ≥18 |
| 8 | Heat shock test | ||||
| Test temperature | ℃ | 130±3 | 130±3 | 130±3 | |
| Test time | h | 1 | 1 | 1 | |
| Experimental result | — | No cracking | No cracking | No cracking | |
| 9 | Impact embrittlement temperature | ||||
| Test temperature | ℃ | -25 | -25 | -25 | |
| Experimental result | Number | ≤15/30 | ≤15/30 | ≤15/30 | |
| 10 | Ozone resistance test | ||||
| Test temperature | ℃ | — | 25±2 | 25±2 | |
| Experiment time | h | — | 24 | 24 | |
| Ozone concentration | ppm | — | 250~300 | 250~300 | |
| Experimental result | — | — | No cracking | No cracking | |
| 11 | Hot water immersion test | ||||
| Test temperature | ℃ | — | 70±2 | 70±2 | |
| Experiment time | h | — | 168 | 168 | |
| Maximum rate of change of tensile strength | % | — | ±30 | ±30 | |
| Maximum rate of change of elongation at break | % | — | ±35 | ±35 | |
| 12 | Oxygen index | % | ≥28 | ≥30 | ≥30 |
| 13 | Smoke density | ||||
| flameless | — | ≤350 | ≤350 | ≤350 | |
| flaming | — | ≤100 | ≤100 | ≤100 | |
| 14 | Combustion releases gas acidity | ||||
| HCI and HBr content | % | ≤0.5 | ≤0.5 | ≤0.5 | |
| HF content | % | ≤0.1 | ≤0.1 | ≤0.1 | |
| pH value | — | ≥4.3 | ≥4.3 | ≥4.3 | |
| Electric conductivity | μS/mm | ≤10 | ≤10 | ≤10 | |
| 15 | Material smoke toxicity hazards | According to the application requirements, negotiated by the supply and demand parties. | |||
CERTIFICATIONS
FAQ
What are the main features of this halogen-free cable material?
The material offers low smoke combustion, high flame retardancy, low toxicity, high temperature resistance, excellent weather resistance, high dielectric properties, and is environmentally friendly.
What is the typical scope of use for these materials?
They are widely used in standard cables, optical cables, coaxial cables, network cables, elevator cables, and various other industrial applications.
Does this cable material contain harmful halogens?
No, it is a halogen-free material. It does not contain harmful halogen compounds, which helps reduce negative environmental impacts and improves safety during a fire.
Can this material withstand high-temperature environments?
Yes, it features high temperature resistance, maintaining stable performance even in demanding high-temperature industrial environments.
What is the tensile strength requirement for the WDZ-Y-J70 model?
According to our testing standards, the tensile strength requirement for the WDZ-Y-J70 material is ≥10.0 MPa.
How is the material's smoke toxicity hazard determined?
The material smoke toxicity hazards are evaluated and negotiated by the supply and demand parties based on the specific application requirements of the final product.