Low Smoke Zero Halogen Coaxial Cable Material from China Suppliers - High-Quality Factory Solutions
Product Features
Scope of Use
Test Items and Standards
Properties of halogen-free low smoke flame retardant thermoplastic polyolefin insulating materials and sheathing materials.
| No. | Inspection item | Unit | Requirements | ||
|---|---|---|---|---|---|
| WDZ-Y-J70 | WDZ-Y-H70 | WDZ-Y-H90 | |||
| 1 | Tensile strength | MPa | ≥10.0 | ≥10.0 | ≥10.0 |
| 2 | Elongation at break | % | ≥160 | ≥160 | ≥160 |
| 3 | Air aging chamber | ||||
| Aging temperature | ℃ | 100±2 | 100±2 | 110±2 | |
| Aging time | h | 168 | 168 | 240 | |
| Maximum rate of change of tensile strength | % | ±25 | ±25 | ±25 | |
| Maximum rate of change of elongation at break | % | ±25 | ±25 | ±25 | |
| 4 | Thermal deformation | ||||
| Test temperature | ℃ | 90±2 | 90±2 | 90±2 | |
| Experimental result | % | ≤50 | ≤50 | ≤50 | |
| 5 | 20℃ volume resistivity | Ω·m | ≥1.0×1012 | ≥1.0×1010 | ≥1.0×1010 |
| 6 | Volume resistivity at operating temperature | ||||
| Test temperature | ℃ | 70±1 | — | — | |
| Volume resistivity | Ω·m | ≥2.0×108 | — | — | |
| 7 | Dielectric strength | MV/m | ≥20 | ≥18 | ≥18 |
| 8 | Heat shock test | ||||
| Test temperature | ℃ | 130±3 | 130±3 | 130±3 | |
| Test time | h | 1 | 1 | 1 | |
| Experimental result | — | No cracking | No cracking | No cracking | |
| 9 | Impact embrittlement temperature | ||||
| Test temperature | ℃ | -25 | -25 | -25 | |
| Experimental result | Number | ≤15/30 | ≤15/30 | ≤15/30 | |
| 10 | Ozone resistance test | ||||
| Test temperature | ℃ | — | 25±2 | 25±2 | |
| Experiment time | h | — | 24 | 24 | |
| Ozone concentration | ppm | — | 250~300 | 250~300 | |
| Experimental result | — | — | No cracking | No cracking | |
| 11 | Hot water immersion test | ||||
| Test temperature | ℃ | — | 70±2 | 70±2 | |
| Experiment time | h | — | 168 | 168 | |
| Maximum rate of change of tensile strength | % | — | ±30 | ±30 | |
| Maximum rate of change of elongation at break | % | — | ±35 | ±35 | |
| 12 | Oxygen index | % | ≥28 | ≥30 | ≥30 |
| 13 | Smoke density | ||||
| flameless | — | ≤350 | ≤350 | ≤350 | |
| flaming | — | ≤100 | ≤100 | ≤100 | |
| 14 | Combustion releases gas acidity | ||||
| HCI and HBr content | % | ≤0.5 | ≤0.5 | ≤0.5 | |
| HF content | % | ≤0.1 | ≤0.1 | ≤0.1 | |
| pH value | — | ≥4.3 | ≥4.3 | ≥4.3 | |
| Electric conductivity | μS/mm | ≤10 | ≤10 | ≤10 | |
| 15 | Material smoke toxicity hazards | According to the application requirements, negotiated by the supply and demand parties. | |||
Certifications
Frequently Asked Questions (FAQ)
What are the main advantages of this cable material?
The material offers low smoke combustion, high flame retardancy, low toxicity, excellent temperature and weather resistance, and high dielectric properties.
What is the typical scope of use for these materials?
They are widely used in optical cables, coaxial cables, network cables, and elevator cables. Special variations are also used in automotive wires, water pipes, and injection molding products.
Is this material environmentally friendly?
Yes, it is entirely halogen-free and does not contain harmful halogen compounds, which helps reduce negative impacts on the environment.
What is the required tensile strength for WDZ-Y-J70 and WDZ-Y-H70?
According to our test standards, the tensile strength requirement for these materials is ≥10.0 MPa.
How does the material perform against ultraviolet (UV) light?
It possesses strong anti-ultraviolet attenuation characteristics, which significantly extends the service life of the cable when exposed to sunlight.
What is the elongation at break standard for these products?
The elongation at break must be ≥160% across the WDZ-Y-J70, WDZ-Y-H70, and WDZ-Y-H90 standards.